Space charge limited current mechanism in Bi2S3 nanowires
Artikel i vetenskaplig tidskrift, 2016
We report on the charge transport properties of individual Bi2S3 nanowires grown within the pores of anodized aluminum oxide templates. The mean pore diameter was 80 nm. Space charge limited current is the dominating conduction mechanism at temperatures below 160 K. Characteristic parameters of nanowires, such as trap concentration and trap characteristic energy, were estimated from current-voltage characteristics at several temperatures.
temperature-dependence
arrays
growth
crystals
transport
memristor
density
electrical characterization
single
gaas nanowires
Författare
Gunta Kunakova
Latvijas Universitate
R. Viter
Latvijas Universitate
Simon Abay
Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik
S. Biswas
Tyndall National Institute at National University of Ireland, Cork
JD. Holmes
Tyndall National Institute at National University of Ireland, Cork
Thilo Bauch
Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik
Floriana Lombardi
Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik
D. Erts
Latvijas Universitate
Journal of Applied Physics
0021-8979 (ISSN) 1089-7550 (eISSN)
Vol. 119 11 114308Ämneskategorier
Den kondenserade materiens fysik
DOI
10.1063/1.4944432