Investigation of the Evolution of the Oxide Scale Formed on 310 Stainless Steel Oxidized at 600 °C in Oxygen with 40% Water Vapour Using FIB and TEM

Fang Liu (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Jun Eu Tang (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Henrik Asteman (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Jan-Erik Svensson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Lars-Gunnar Johansson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Mats Halvarsson (Institutionen för teknisk fysik, Mikroskopi och mikroanalys)
Oxidation of Metals (0030-770X). Vol. 71 (2009), 1-2, p. 77-105.
[Artikel, refereegranskad vetenskaplig]

Detailed microstructure investigations were performed on oxide scales formed on 310 stainless steel exposed isothermally at 600 °C to O2 with 40% water vapour for 1–336 h. FIB microscopy was used to study the evolution of the surface morphology and to prepare cross-section TEM thin foils of the oxide scales. The foils were investigated by analytical transmission electronmicroscopy. The results showed that a thin protective base oxide scale had formed after 1 h. Due to Cr loss from the oxide scale through water vapour induced Cr evaporation, local breakaway oxidation occurs, resulting in the formation of oxide nodules. The development of these nodules depends on whether a new Cr-rich healing layer is formed or not. A model for the evolution of the oxide scale is proposed based on the results regarding the composition and distribution of various phases in the oxide scale and subjacent steel.

Nyckelord: Fe–Cr–Ni alloy, High temperature oxidation, Water vapour, Microstructure, FIB, TEM, EDX



Denna post skapades 2009-03-04. Senast ändrad 2013-10-29.
CPL Pubid: 90977

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)
Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)

Ämnesområden

Övrig teknisk materialvetenskap

Chalmers infrastruktur