The effect of growth temperature on the nanostructure and dielectric response of BaTiO3 ferroelectric films

John Berge (Institutionen för mikroteknologi och nanovetenskap, Mikrovågs- och terahertzteknologi) ; Andrei Vorobiev (Institutionen för mikroteknologi och nanovetenskap, Mikrovågs- och terahertzteknologi) ; Spartak Gevorgian (Institutionen för mikroteknologi och nanovetenskap, Mikrovågs- och terahertzteknologi)
Thin Solid Films Vol. 515 (2007), 16, p. 6302-6308.
[Artikel, refereegranskad vetenskaplig]

BaTiO3 ferroelectric films were grown on Si/SiO2/Ti/Pt/Au/Pt templates at different temperatures in the range 560-680 degrees C by pulsed laser deposition. Cross section scanning electron microscopy images and atomic force microscopy surface morphology analysis reveal films with columnar structure and in-plane grain size distribution, in the range 10-60 nm, depending on growth temperature. Low-field dielectric measurements were performed as functions of temperature in the range 40-500 K and extemal dc field up to 400 kV/cm. The apparent permittivity of ferroelectric films grown at 680 degrees C shows Curie-Weiss behavior above 400 K with Curie temperature and Curie-Weiss constant 240 K and 1 center dot 10(5) K, respectively. The films grown at lower temperatures reveal a decrease of Curie temperature down to - 80 K, reduced values of apparent permittivity and loss tangent, and broadening of maximum of temperature dependence of apparent permittivity. The film grown at 590 degrees C demonstrates state of the art combination of temperature stability (temperature coefficient of apparent permittivity 300 ppm/K in the range 50350 K), high tunability of apparent permittivity (up to 60% at room temperature), and relatively low loss tangent (less than 0.05 in the frequency range up to 10 GHz). The change in apparent permittivity and its temperature dependence, with variation of growth temperature are analyzed using two different composite models. The first model assumes the film to be a composite with vertical inclusions of low permittivity dielectric material associated with grain boundaries. This model may explain the observed decrease of permittivity with decreasing growth temperature, but not the shift of Curie temperature. The second model assumes a layered type of composite with low permittivity material associated with the film/ electrode interfaces, and allows explanation of the Curie temperature shift. (C) 2006 Elsevier B.V. All rights reserved.



Denna post skapades 2008-12-23. Senast ändrad 2014-09-02.
CPL Pubid: 82738

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Mikrovågs- och terahertzteknologi (2006-2007)

Ämnesområden

Fysik

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:


Tunable Bulk Acoustic Wave Resonators Based on BaxSr1-xTiO3 Thin Films


Switchable and tunable bulk acoustic wave resonators based on BaxSr1-xTiO3 thin films