Conductivity and antiferromagnetism of CaCuO2 thin films doped by Sr

Gennady A. Ovsyannikov (Institutionen för mikroteknologi och nanovetenskap) ; V. V. Demidov ; Y. V. Kislinski ; Philipp Komissinskiy (Institutionen för mikroteknologi och nanovetenskap) ; Dag Winkler (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik)
Physica C: Superconductivity Vol. 460-462 (2007), Part 1, 1 September 2007, p. 536-537.
[Artikel, refereegranskad vetenskaplig]

The results of electrical and magnetic investigations of epitaxial CaxSr1-xCuO2 (CSCO) thin films grown by pulsed laser deposition are presented. The experimental temperature dependence of the CSCO film conductivity at low doping level is well described by the 3-d Mott insulator model over a wide temperature range (4.2-300 K). A deviation from the model with changing of Sr concentration has been observed. The Neel temperature of the films, T-N, was determined by electron paramagnetic resonance technique. The comparison of the obtained TN value with the one previously obtained for the CSCO powder sample could be caused by oxygen vacancies in the CSCO films. Nb/Au/Ca1-xSrxCuO2/YBa2Cu3O7-delta heterostructures have been fabricated and superconducting current has been observed at low temperatures. (c) 2007 Elsevier B.V. All rights reserved.


Proceedings of the 8th International Conference on Materials and Mechanisms of Superconductivity and High Temperature Superconductors - M2S-HTSC VIII



Denna post skapades 2008-12-19. Senast ändrad 2014-11-10.
CPL Pubid: 82365

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)