The effects of mineral additions on chloride penetration into concrete under the frost action

Bo Li (Institutionen för bygg- och miljöteknik, Byggnadsteknologi) ; Luping Tang (Institutionen för bygg- och miljöteknik, Byggnadsteknologi)
Proceedings of IALCCE08 - First International Symposium on Life-Cycle Civil Engineering p. 189-194. (2008)
[Konferensbidrag, refereegranskat]

This paper presents the results from a study of the effects of mineral additions on chloride penetration into concrete under the frost action. Mineral additions namely fly-ash (FA), silica fume (SF), GGBF slag (SL) were used to replace some part of cement in concrete. Seven types of concrete were investigated. All specimens were immersed in tap water or NaCl solutions under the freeze-thaw (F-T) and the climate room conditions. The results showed that the frost action significantly increase liquid uptake in both plain Portland cement concrete and concrete with mineral additions whatever specimens were exposed to tap water or salt solutions. Incorporation of mineral additions in concrete can in general reduce the amount of uptaken liquid. As a conclusion, incorporation of mineral additions and proper entraining air pores in concrete can improve resistance of concrete to chloride penetration even under the frost action.



Denna post skapades 2008-12-18. Senast ändrad 2017-03-21.
CPL Pubid: 82218

 

Institutioner (Chalmers)

Institutionen för bygg- och miljöteknik, Byggnadsteknologi (2005-2017)

Ämnesområden

Samhällsbyggnadsteknik

Chalmers infrastruktur