Cyclic oxidation of two FeCrAlRE foils at 1100 oC - The influence of the concentration of minor alloying elements on scale microstructure

Fang Liu (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Helena Götlind (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Sead Canovic (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Haiping Lai (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Jörgen Westlinder ; Andreas Rosberg ; Jan-Erik Svensson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Lars-Gunnar Johansson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Mats Halvarsson (Institutionen för teknisk fysik, Mikroskopi och mikroanalys)
Materials Science Forum: 7th International Symposium on High Temperature Corrosion and Protection of Materials; Les Embiez; France; 18 May 2008 through 23 May 2008 Vol. 595-598 (2008), p. 707-716.
[Konferensbidrag, refereegranskat]

Two FeCrAlRE alloys, a commercial, 0C404, and a model alloy in the form of thin foils, with different Mn, Nb, Mo and Ti concentrations were subjected to cyclic oxidation in lab air at 1100°C. The oxidized samples were studied by gravimetry, Grazing-Incidence X-ray Diffraction (GI-XRD), Scanning Transmission Electron Microscopy (STEM), and Energy Dispersive X-ray (EDX) analysis. The two FeCrAl alloys exhibit different oxidation kinetics; however, both alloys have the same weight gain after 500 hours exposure. During the early stages the scale consists mainly of α-Al2O3 together with some oxide particles containing Mn, Al, Fe and Cr formed on the alloys. After 500 hours the 0C404 scale locally also consists of larger polycrystalline regions of Mn-Cr-Al spinel. In addition, Si-rich oxide, chromia and Al-Cr oxide could be observed at the metal/oxide interface.



Denna post skapades 2008-12-16. Senast ändrad 2016-08-18.
CPL Pubid: 81654

 

Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)
Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)

Ämnesområden

Övrig teknisk materialvetenskap

Chalmers infrastruktur