Influence of iron addition on the oxygen-deficient Sr0.85Bi0.15Co1-xFexO3-d (0.0
Annika K. Eriksson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi) ; Christopher S Knee ; Sten G. Eriksson (Institutionen för kemi- och bioteknik, Oorganisk miljökemi)
Journal of Solid state chemistry (0022-4596). Vol. 181 (2008), p. 2031-2040.
[Artikel, refereegranskad vetenskaplig]

A series of oxygen-deficient Sr0.85Bi0.15Co1-xFexO3-d (0.00.8. Evidence of weak superstructures, reflecting local oxygen ordering, is also obtained from electron diffraction. For all oxygen-annealed phases the average structure reverts to cubic Pm-3m. The as-prepared samples show G-type antiferromagnetic order at room temperature. The oxygen annealed x = 0.10, 0.25 and 1.0 samples display low-temperature spin-glass transitions.

Nyckelord: Perovskite, Oxygen vacancies, Supercell, Spin glass, Neutron diffraction

Denna post skapades 2008-11-28. Senast ändrad 2010-03-16.
CPL Pubid: 79205


Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Oorganisk miljökemi (2005-2014)
Institutionen för kemi (2001-2011)


Fasta tillståndets kemi

Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Interplay between structure and properties in perovskite related materials