Characterization of Adhesion Strength of HVOF Sprayed IN718 Coatings

Christophe Lyphout (Institutionen för material- och tillverkningsteknik) ; Per Nylén ; Uta Klement (Institutionen för material- och tillverkningsteknik) ; Mohammad Sattari (Institutionen för material- och tillverkningsteknik)
Proceedings of the 22nd International Conference on Surface Modification Technologies (SMT22), Trollhättan, Sweden p. 11-18. (2009)
[Konferensbidrag, refereegranskat]

The tensile adhesion strength of thermally sprayed coating is conventionally evaluated via the ASTM C633-69 standard. The maximum measurable adhesion is then limited by the adhesion strength of the polymer media. High velocity oxy-fuel (HVOF) spraying can exhibit very high bonding strength and thus it is essential to develop an alternative method to evaluate coating adhesion strength. In this work a Modified Tensile Adhesion Test (MTAT) is proposed replacing gluing with induction brazing. The method was evaluated for HVOF sprayed Inconel 718 coatings deposited on Inconel 718 substrates. The effect of induction brazing process and the characteristics of the braze-coating interface was given particular interest. The results indicate that the method is superior to the ASTM C633-69 for characterisation of adhesion of coatings with high bond strength.

Nyckelord: Thermal Spraying Process, Coating Adhesion Strength, HVOF, Inconel 718, Tensile Adhesion Test, ASTM C633-69, Induction Brazing, Bonding Mechanisms, Coating Thickness, Braze Joint Strength.

Denna post skapades 2008-11-13. Senast ändrad 2014-09-02.
CPL Pubid: 77838


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik (2005-2017)



Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Adhesion and Residual Stress Characterization of HVOF Sprayed Inconel 718 Coatings

Adhesion strength of HVOF sprayed Inconel 718 coatings