I. A. Kowalik ; B. J. Kowalski ; R. J. Iwanowski ; K. Kopalko ; E. Lusakowska ; M. Sawicki ; J. Sadowski ; Martin Adell (Institutionen för teknisk fysik, Fasta tillståndets fysik) ; I. Grzegory ; S. Porowski
Physical Review B (1098-0121). Vol. 75 (2007), 23, p. 11.
[Artikel, refereegranskad vetenskaplig]

MnAs has been grown by means of MBE on the GaN(000 (1) over bar)-(1x1) surface. Two options of initiating the crystal growth were applied: (a) a regular MBE procedure (manganese and arsenic were delivered simultaneously) and (b) subsequent deposition of manganese and arsenic layers. It was shown that spontaneous formation of MnAs dots with the surface density of 1x10(11) cm(-2) and 2.5x10(11) cm(-2), respectively (as observed by atomic force microscopy), occurred for the layer thickness higher than 5 ML. Electronic structure of the MnAs/GaN systems was studied by resonant photoemission spectroscopy. That led to determination of the Mn 3d-related contribution to the total density of states distribution of MnAs. It has been proven that the electronic structures of the MnAs dots grown by the two procedures differ markedly. One corresponds to metallic, ferromagnetic NiAs-type MnAs, the other is similar to that reported for half-metallic zinc-blende MnAs. Both systems behave superparamagnetically (as revealed by magnetization measurements), but with both the blocking temperatures and the intradot Curie temperatures substantially different. The intradot Curie temperature is about 260 K for the former system while markedly higher than room temperature for the latter one. Relations between growth process, electronic structure, and other properties of the studied systems are discussed. Possible mechanisms of half-metallic MnAs formation on GaN are considered.


Denna post skapades 2008-11-07. Senast ändrad 2016-09-29.
CPL Pubid: 77274


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Fasta tillståndets fysik (2005-2015)


Teknisk fysik

Chalmers infrastruktur