Nucleation and aligned growth of multi-wall carbon nanotube films during thermal CVD

Yiming Yao (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Lena K. L. Falk (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Raluca. E. Morjan ; Oleg Nerushev ; Eleanor E B Campbell
Carbon Vol. 45 (2007), p. 2065-2071.
[Artikel, övrig populärvetenskap]

The development during early growth of a multi-wall carbon nanotube film by thermal CVD with acetylene (C2H2) and hydrogen at 750 °C has been characterized in detail by cross-section transmission electron microscopy. The studies provide information on the nanotube growth mechanisms and the complex catalyst transformations that are essential for the onset of different growth stages. An initial random growth catalysed by supported particles is followed by aerosol growth of aligned tubes. This results in a two-layered film structure, where a film of aligned nanotubes is lifting up an initially formed nanotube network from the substrate.

Nyckelord: carbon nanotube CVD



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2007-12-26. Senast ändrad 2016-10-04.
CPL Pubid: 63878

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)
Institutionen för fysik (GU) (GU)

Ämnesområden

Materialvetenskap
Nanovetenskap och nanoteknik
Fysik
Den kondenserade materiens fysik

Chalmers infrastruktur