Effect of Sigma2 grain boundaries on plastic deformation of WC-Co cemented carbides

Gustaf Östberg (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Muhammad Umar Farooq (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Mikael Christensen (Institutionen för teknisk fysik, Material- och ytteori) ; Hans-Olof Andrén (Institutionen för teknisk fysik, Mikroskopi och mikroanalys) ; Uta Klement (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Göran Wahnström (Institutionen för teknisk fysik, Material- och ytteori)
Mat. Sci. and Eng. A. Vol. 416 (2006), p. 119.
[Artikel, refereegranskad vetenskaplig]

Cutting inserts of WC–6 wt.% Co were investigated before and after plastic deformation. The deformation tests were performed with a turning operation under realistic, yet controlled, conditions. SEM studies showed that after deformation the WC skeleton structure had broken up and thin lamellae of binder phase had formed in less than 10% of the grain boundaries. Ab initio calculations showed that ∑2 twist WC/WC boundaries have a high work of separation and the interface energy is not lowered by forming two Co/WC boundaries. Electron backscattered diffraction (EBSD) measurements showed an apparent increase in the relative occurrence of ∑2 boundaries due to poor indexing of the deformed material. The accumulation of dislocations in general boundaries is held responsible for the difficulty in identifying them compared with ∑2 boundaries. At the ∑2 tilt boundary the grains have the glide planes {1 0 -1 0} in common and at the ∑2 twist boundary there are three glide planes intersecting, which facilitate dislocation movements across the ∑2 boundaries.

Nyckelord: EBSD, Cemented carbides, Ab initio calculations, Plastic deformation



Denna post skapades 2007-12-20. Senast ändrad 2015-03-30.
CPL Pubid: 63617

 

Institutioner (Chalmers)

Institutionen för teknisk fysik, Mikroskopi och mikroanalys (2005-2012)
Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)
Institutionen för teknisk fysik, Material- och ytteori (1900-2015)

Ämnesområden

Den kondenserade materiens fysik

Chalmers infrastruktur