Microscopic structure of tin-borate and tin-boratephosphate glasses

Cecilia Gejke (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Ezio Zanghellini (Institutionen för experimentell fysik, Materialfysik) ; Jan Swenson (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Lars Börjesson (Institutionen för teknisk fysik, Kondenserade materiens fysik)
Journal of Power Sources (0378-7753). Vol. 119-121 (2003), p. 576-580..
[Artikel, refereegranskad vetenskaplig]

The structure of tin-borate and tin-borophosphate glasses has been examined with diffuse reflectance IR (DR-IR) and Raman spectroscopy. The basic network structure for these glasses is described as well as the positioning of tin in the network. Data suggests that the amount of phosphate present in the glass regulate the glass forming properties of tin. With borate as the dominating glass forming oxide, SnO acts like a glass former, but with increasing amount of phosphate SnO instead tends to behave as a network modifier.

Nyckelord: Amorphous, Tin, FT-IR, Raman spectroscopy

Denna post skapades 2007-04-19. Senast ändrad 2017-10-03.
CPL Pubid: 40694


Institutioner (Chalmers)

Institutionen för teknisk fysik, Kondenserade materiens fysik (1900-2015)
Institutionen för experimentell fysik, Materialfysik (1997-2004)


Struktur- och vibrationsfysik
Mesoskopisk fysik

Chalmers infrastruktur