The effect of lithium insertion on the structure of tin oxide-based glasses

Cecilia Gejke (Institutionen för teknisk fysik, Kondenserade materiens fysik) ; Ezio Zanghellini (Institutionen för experimentell fysik, Materialfysik) ; L. Fransson ; K. Edström ; Lars Börjesson (Institutionen för teknisk fysik, Kondenserade materiens fysik)
Journal of Power Sources (0378-7753). Vol. 97-98 (2001), p. 226-228..
[Artikel, refereegranskad vetenskaplig]

Two different SnO-based glasses, Sn2B3O6.5 and Sn2B2AlO6.5, have been examd. with FT-IR and Raman spectroscopy at different stages during the first electrochemical cycle. Some disruption of the connection between borate units in the network occurred during cycling. There was also an irreversible formation of Li3BO3 that can be related to the large capacity loss.

Nyckelord: Anode, Amorphous, Tin, FT-IR, Raman spectroscopy



Denna post skapades 2007-04-19.
CPL Pubid: 40691

 

Institutioner (Chalmers)

Institutionen för teknisk fysik, Kondenserade materiens fysik (1900-2015)
Institutionen för experimentell fysik, Materialfysik (1997-2004)

Ämnesområden

Struktur- och vibrationsfysik
Mesoskopisk fysik
Spektroskopi
Elektrokemi
Spektroskopi
Kemisk fysik
Materialkemi

Chalmers infrastruktur