Electron backscatter diffraction characterization of fatigue crack growth in laser metal wire deposited Ti-6Al-4V

Pia Åkerfeldt ; Magnus Hörnqvist Colliander (Institutionen för fysik, Materialens mikrostruktur (Chalmers)) ; Robert Pederson ; Marta-Lena Antti
Materials Characterization (1044-5803). Vol. 135 (2018), p. 245-256.
[Artikel, refereegranskad vetenskaplig]

By additive manufacturing (AM) there is a feasibility of producing near net shape components in basically one step from 3D CAD model to final product. The interest for AM is high and during the past decade a lot of research has been carried out in order to understand the influence from process parameters on the microstructure and furthermore on the mechanical properties. In the present study laser metal wire deposition of Ti-6Al-4V has been studied in detail with regard to its fatigue crack propagation characteristics. Two specimen orientations, parallel and perpendicular to the deposition direction, have been evaluated at room temperature and at 250 °C. No difference in the fatigue crack growth rate could be confirmed for the two specimen orientations. However, in the fractographic study it was observed that the tortuosity varied between certain regions on the fracture surface. The local crack path characteristic could be related to the alpha colony size and/or the crystallographic orientation. Moreover, large areas exhibiting similar crystallographic orientation were observed along the prior beta grain boundaries, which were attributed to the wide alpha colonies frequently observed along the prior beta grain boundaries.



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-12-14. Senast ändrad 2017-12-14.
CPL Pubid: 253778

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)