The trade-off between electrochromic stability and contrast of a thiophene-Quinoxaline copolymer

X. Xing ; C. F. Wang ; X. J. Liu ; L. Q. Qin ; Ergang Wang (Institutionen för kemi och kemiteknik, Polymerteknologi) ; F. L. Zhang
Electrochimica Acta (0013-4686). Vol. 253 (2017), p. 530-535.
[Artikel, refereegranskad vetenskaplig]

The stability of organic electrochromic devices is a crucial issue for their applications. However, until now the degradation mechanism of electrochromic materials are still not fully understood especially for electrochromic conjugated polymers (ECPs). To improve device stability, intensive investigation on the degradation mechanism of ECPs is urgently needed. Here we report our study on the electrochromic degradation in a thiophene-quinoxaline copolymer: poly [2,3-bis-(3-octyloxyphenyl) quinoxaline-5,8diyl- alt-thiophene-2,5-diyl] (TQ1). The results of X-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectra (UPS) and UV-vis transmission spectra reveal that there are three main factors during the electrochromic degradation of TQ1. The first one is anion (ClO4-) irreversibly deep trapped, while the second is peroxidation of the thiophene group in TQ1. Both factors reduce the conductivity and electrochromism of TQ1. The third is structural relaxation resulting lager conjugated system of TQ1 molecules in film, which is gradually developed during 400 cycling of CV at a narrow potential range (01 V). When a potential range 0-0.7 V is applied, all three factors are prohibited, no electrochromism degradation is observed anymore, although the contrast becomes smaller. Our investigation systematically discloses the degradation mechanism during the electrochemistry processing of a ECP (TQ1), demonstrating the significance of trade-off between the electrochromic stability and contrast of the ECP.

Nyckelord: Electrochemistry, Electrochromic, Degradation, Stability, Thiophene-quinoxaline copolymer



Denna post skapades 2017-11-10. Senast ändrad 2017-11-13.
CPL Pubid: 253052

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Polymerteknologi

Ämnesområden

Materialkemi

Chalmers infrastruktur