Josephson effect through YBa2Cu3 O7-δ /Au-encapsulated nanogaps

Reza Baghdadi (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; Simon Abay ; Dmitri Golubev ; Thilo Bauch (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; Floriana Lombardi (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik)
Physical Review B (2469-9950). Vol. 95 (2017), 17,
[Artikel, refereegranskad vetenskaplig]

We successfully fabricated and studied planar superconductor-normal-superconductor (SNS) Josephson junctions made of YBa2Cu3O7-? (YBCO) high-TC superconductor (S) and Au normal metal (N). The crucial step in fabrication was done by using a Pt/Au bilayer encapsulation of the patterned YBCO nanogap. This procedure preserves the YBCO nanogap from the degradation due to the contact with resists, water, and chemicals involved in further processing for hybrid devices. The junctions exhibit Fraunhofer-like modulation patterns and Shapiro steps when they are irradiated by a rf field. Furthermore, we analyzed the IC(T) characteristics of our hybrid junctions employing a SINI?S (superconductor-insulator-normal conductor-insulator-superconductor) model.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-10-03. Senast ändrad 2017-10-10.
CPL Pubid: 252227


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik


Nanovetenskap och nanoteknik

Chalmers infrastruktur