Effect of shot peening on the residual stress and mechanical behaviour of low-temperature and high-temperature annealed martensitic gear steel 18CrNiMo7-6

R. Yang ; X. Zhang ; Dinesh Mallipeddi (Institutionen för industri- och materialvetenskap, Material- och tillverkningsteknik) ; N. Angelou ; H.L. Toftegaard ; Y. Li ; Johan Ahlström (Institutionen för industri- och materialvetenskap, Konstruktionsmaterial) ; L. Lorentzen ; G. Wu ; X. Huang
IOP Conference Series: Materials Science and Engineering. 38th Riso International Symposium on Materials Science, Riso, Denmark, 4-8 September 2017 (1757-8981). Vol. 219 (2017), 1, p. Art no: UNSP 012046.
[Konferensbidrag, refereegranskat]

A martensitic gear steel (18CrNiMo7-6) was annealed at 180 °C for 2h and at ∼ 750 °C for 1h to design two different starting microstructures for shot peening. One maintains the original as-transformed martensite while the other contains irregular-shaped sorbite together with ferrite. These two materials were shot peened using two different peening conditions. The softer sorbite + ferrite microstructure was shot peened using 0.6 mm conditioned cut steel shots at an average speed of 25 m/s in a conventional shot peening machine, while the harder tempered martensite steel was shot peened using 1.5 mm steel shots at a speed of 50 m/s in an in-house developed shot peening machine. The shot speeds in the conventional shot peening machine were measured using an in-house lidar set-up. The microstructure of each sample was characterized by optical and scanning electron microscopy, and the mechanical properties examined by microhardness and tensile testing. The residual stresses were measured using an Xstress 3000 G2R diffractometer equipped with a Cr Kα x-ray source. The correspondence between the residual stress profile and the gradient structure produced by shot peening, and the relationship between the microstructure and strength, are analyzed and discussed.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-09-11. Senast ändrad 2017-11-20.
CPL Pubid: 251812


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)