High-performance ternary polymer solar cells from a structurally similar polymer alloy

W. F. Shen ; W. C. Chen ; D. Q. Zhu ; J. D. Zhang ; Xiaofeng Xu (Institutionen för kemi och kemiteknik, Polymerteknologi) ; H. X. Jiang ; T. Wang ; Ergang Wang (Institutionen för kemi och kemiteknik, Polymerteknologi) ; R. Q. Yang
Journal of Materials Chemistry A (2050-7488). Vol. 5 (2017), 24, p. 12400-12406.
[Artikel, refereegranskad vetenskaplig]

High-efficiency ternary polymer solar cells (PSCs) are fabricated by using two donor polymers (PBDTTPD and PBDTTT-C-T) with similar polymer backbones and complementary absorption and PC71BM as the acceptor. A high power conversion efficiency (PCE) of 9.3% is achieved with a high short-circuit current density (J(sc)) of 17.2 mA cm(-2). The enhanced J(sc) and PCEs are mainly attributed to the broadened photoresponse of the ternary blend. Good miscibility of the two donor polymers is found due to the similar polymer main chains, leading to the desired morphology between the donors and PC71BM in the ternary blends. The trend of open-circuit voltage (V-oc) variations indicates the formation of a polymer alloy in this ternary blend. Our work demonstrates that using two donor polymers with similar backbone structures is a rational strategy for realizing high-performance ternary PSCs.

Nyckelord: Power Conversion Efficiency, Small-Molecule, Nonfullerene Acceptors, 11-Percent Efficiency, Ir Sensitization, Energy-Transfer, Fullerene, Chains



Denna post skapades 2017-07-26.
CPL Pubid: 250796

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Polymerteknologi

Ämnesområden

Materialkemi

Chalmers infrastruktur