Porosity measurements in suspension plasma sprayed YSZ coatings

Uta Klement (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Johanna Ekberg (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Simone Creci (Institutionen för kemi och kemiteknik, Teknisk ytkemi) ; Stephen T Kelly
Proceedings of Coating Science International (COSi) 2017 p. 118-121. (2017)
[Konferensbidrag, refereegranskat]

A large variety of coatings are used to protect structural engineering materials from corrosion, wear, and erosion, and to provide thermal insulation. In this work yttria-stabilized zirconia (YSZ) coatings produced by suspension plasma spraying (SPS) were investigated with respect to their microstructure and especially their porosity, as the porosity affects the thermal insulation of the underlying component. To determine porosity, pore size distribution and pore shape, the coatings were investigated using novel advanced characterization techniques like NMR cryoporometry and X-ray microscopy. In general, the porosity is inhomogeneously distributed and the coatings showed a large variety of pore sizes ranging from a few nanometers to micrometers.

Nyckelord: porosity, TBC, YSZ, suspension plasma spray, NMR cryoporometry, X-ray microscopy



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-07-06.
CPL Pubid: 250545

 

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)
Institutionen för kemi och kemiteknik, Teknisk ytkemi

Ämnesområden

Materialvetenskap
Hållbar utveckling
Materialteknik

Chalmers infrastruktur