Polar Side Chains Enhance Processability, Electrical Conductivity, and Thermal Stability of a Molecularly p-Doped Polythiophene.

Renee Kroon (Institutionen för kemi och kemiteknik, Polymerteknologi) ; David Kiefer (Institutionen för kemi och kemiteknik, Polymerteknologi) ; Dominik Stegerer (Institutionen för kemi och kemiteknik, Polymerteknologi) ; Liyang Yu (Institutionen för kemi och kemiteknik, Polymerteknologi) ; Michael Sommer ; Christian Müller (Institutionen för kemi och kemiteknik, Polymerteknologi)
Advanced materials (Deerfield Beach, Fla.) (1521-4095). Vol. 29 (2017), 24, p. 1700930.
[Artikel, refereegranskad vetenskaplig]

Molecular doping of organic semiconductors is critical for optimizing a range of optoelectronic devices such as field-effect transistors, solar cells, and thermoelectric generators. However, many dopant:polymer pairs suffer from poor solubility in common organic solvents, which leads to a suboptimal solid-state nanostructure and hence low electrical conductivity. A further drawback is the poor thermal stability through sublimation of the dopant. The use of oligo ethylene glycol side chains is demonstrated to significantly improve the processability of the conjugated polymer p(g4 2T-T)-a polythiophene-in polar aprotic solvents, which facilitates coprocessing of dopant:polymer pairs from the same solution at room temperature. The use of common molecular dopants such as 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ) and 2,3-dichloro-5,6-dicyano-1,4-benzoquinone (DDQ) is explored. Doping of p(g4 2T-T) with F4TCNQ results in an electrical conductivity of up to 100 S cm(-1) . Moreover, the increased compatibility of the polar dopant F4TCNQ with the oligo ethylene glycol functionalized polythiophene results in a high degree of thermal stability at up to 150 °C.

Nyckelord: electrical conductivity; molecular dopants; polythiophenes; organic semiconductors



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-06-27. Senast ändrad 2017-07-26.
CPL Pubid: 250118

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Polymerteknologi

Ämnesområden

Materialvetenskap
Polymerteknologi

Chalmers infrastruktur