Investigating correlations between crack width, corrosion level and anchorage capacity

Mohammad Tahershamsi (Institutionen för bygg- och miljöteknik, Konstruktionsteknik) ; Ignasi Fernandez Perez (Institutionen för bygg- och miljöteknik, Konstruktionsteknik) ; Karin Lundgren (Institutionen för bygg- och miljöteknik, Konstruktionsteknik) ; Kamyab Zandi Hanjari (Institutionen för bygg- och miljöteknik, Konstruktionsteknik)
Structure and Infrastructure Engineering (1573-2479). Vol. 13 (2017), 10, p. 1294-1307.
[Artikel, refereegranskad vetenskaplig]

In assessing existing structures, inspection results need to be linked to the effects on load-carrying capacity; to provide such information, this study has investigated the correlation between splitting crack width, corrosion level and anchorage capacity. The study was based on 13 reinforced concrete beams that had been exposed to natural corrosion for 32 years, eleven beams with splitting cracks and two without. The crack pattern and widths were documented before undergoing structur-al testing of anchorage capacity. Thereafter, the reinforcement bars were extracted and their corro-sion levels measured using two methods, gravimetric weight loss and 3D scanning. The corrosion level from the weight loss method was approximately twice as large; possible reasons are horizon-tal or subsurface corrosion pits, and the cleaning method. Further, for the same corrosion level, the specimens in this study had much larger crack widths and slightly lower bond capacity than the artificially corroded tests in the literature; a possible reason is that these specimens had been sub-jected to combined corrosion and freezing. However, the corrosion level and reduction in bond ca-pacity related to crack width were both lower in the present than in previous studies in the litera-ture. Thus, by formulating a damage indicator from the damage visible in the form of crack widths from artificial test data, the structural capacity is estimated to be on the safe side.

Nyckelord: Natural corrosion, inspection, bond, anchorage, crack width, pitting corrosion, 3D optical scanning

Full text can be downloaded at http://www.tandfonline.com/eprint/TQjMa7kmhP6HYWyXGgsx/full

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-05-10. Senast ändrad 2017-08-15.
CPL Pubid: 249244


Läs direkt!

Filen i embargo till 2017-12-27

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för bygg- och miljöteknik, Konstruktionsteknik (2005-2017)


Building Futures
Hållbar utveckling

Chalmers infrastruktur