Radial tunnel diodes based on InP/InGaAs core-shell nanowires

O. Tizno ; Bahram Ganjipour (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; M. Heurlin ; C. Thelander ; M. T. Borgstrom ; L. Samuelson
Applied Physics Letters (0003-6951). Vol. 110 (2017), 11,
[Artikel, refereegranskad vetenskaplig]

We report on the fabrication and characterization of radial tunnel diodes based on InP(n+)/InGaAs(p+) core-shell nanowires, where the effect of Zn-dopant precursor flow on the electrical properties of the devices is evaluated. Selective and local etching of the InGaAs shell is employed to access the nanowire core in the contact process. Devices with an n+-p doping profile show normal diode rectification, whereas n+-p+ junctions exhibit typical tunnel diode characteristics with peak-to- valley current ratios up to 14 at room temperature and 100 at 4.2 K. A maximum peak current density of 28A/cm(2) and a reverse current density of 7.3 kA/cm(2) at V-SD=-0.5V are extracted at room temperature after normalization with the effective junction area. Published by AIP Publishing.

Denna post skapades 2017-05-03. Senast ändrad 2017-07-07.
CPL Pubid: 249092


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik



Chalmers infrastruktur