Optimized production route of WC powder pre-alloyed with Ta for fine grained cemented carbides

Jonathan Weidow (Institutionen för fysik (Chalmers)) ; E. Halwax ; W. D. Schubert
International Journal of Refractory Metals & Hard Materials (0263-4368). Vol. 62 (2017), Part B, Special Issue, p. 97-103.
[Artikel, refereegranskad vetenskaplig]

Powders of hexagonal (W,Ta)C were produced following a two-step carburization process with (W,Ta)(2)C powder as an intermediate product XRD measurements indicate that higher temperatures during the first carburization step increase the fraction of Ta in the (W,Ta)(2)C structure where lower temperatures during the second carburization step seems to increase the fraction of Ta in the (W,Ta)C structure. Lower temperatures during the carburization steps increase the fraction of Sigma 2 WC/WC grain boundaries and cause the formation of what is interpreted as Sigma 4 boundaries. The (W,Ta)C powders can be successfully used to produce fine grained WC-Co based cemented carbides. The pre-alloying with Ta appears to have a softening effect on the material.

Nyckelord: EBSD, Electron backscatter diffraction, Doping, SEM, Scanning electron microscopy



Denna post skapades 2017-01-20.
CPL Pubid: 247539

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för fysik (Chalmers)

Ämnesområden

Kemi

Chalmers infrastruktur