The influence of gas composition on Pd-based catalyst activity in methane oxidation - inhibition and promotion by NO

Nadezda Sadokhina (Institutionen för kemi och kemiteknik, Kemisk reaktionsteknik ; Kompetenscentrum katalys (KCK)) ; G. Smedler ; U. Nylen ; M. Olofsson ; Louise Olsson (Institutionen för kemi och kemiteknik, Kemisk reaktionsteknik ; Kompetenscentrum katalys (KCK))
Applied Catalysis B-Environmental (0926-3373). Vol. 200 (2017), p. 351-360.
[Artikel, refereegranskad vetenskaplig]

The individual influence, as well as the combined effect of H2O and NO on the activity of Pd/Al2O3, PtPd/Al2O3 and PtPd/CeAl2O3 catalysts in complete methane oxidation under lean conditions were investigated. Under temperature-programmed ramping experiments the activity was severely inhibited in the presence of 5 vol.% H2O in the reaction mixture. We propose that this is due to blocking by both water and hydroxyl species. Under the influence of NO without water in the gas flow, it was found that the methane oxidation activity was partly suppressed, due to blocking of active sites. Indeed TPD performed after ramping experiments showed NOx storage on the catalyst. Contrary to the negative effect of NO in the dry case, the promotional NO effect on the activity was observed when water was co-fed, comparing the case with only water presence. The promotional NO effect was confirmed with isothermal experiments, where e.g. the methane conversion decreased from initial 96% to 25% after 10 h of exposure in CH4-O-2-H2O mixture at 450 degrees C over the Pd/Al2O3 sample, while the decrease was only from 88% to 60% when catalyst was exposed to CH4-O-2-H2O-NO mixture. We propose that the reason is that the NO reacts with the hydroxyl species to form HNO2, which reduces the water deactivation effect.

Nyckelord: Methane oxidation, NO, H2O, Inhibition, Promotion



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-10-28. Senast ändrad 2017-09-14.
CPL Pubid: 244409

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)