A study on the influence of ageing of coatings on their mechanical properties and fracture in ballast tanks

Jonas Ringsberg (Institutionen för sjöfart och marin teknik, Marin teknik)
Ships and Offshore Structures (1744-5302). Vol. 12 (2017), sup 1, p. S268-S279.
[Artikel, refereegranskad vetenskaplig]

Inspections have shown that coatings used in water ballast tanks (WBTs) can fracture prior to their target design life. This has led to local corrosion of the substrate and unwanted maintenance which is time-consuming and costly for the ship owner. The objective of the current study is to show that ageing of marine coatings used in WBTs can reduce the coatings’ fracture strain to a level lower than the strain of the substrate. Laboratory tests were conducted to subject three commercial WBT coatings to different types of ageing. Changes in their mechanical properties were confirmed. Finite element analyses of a 4,400 TEU container vessel were carried out for a number of sea state conditions. The strains of the hull structure (i.e. the substrate) were calculated and compared with the fracture strains of the aged coatings. It was shown that, in many locations, the strain of the substrate can exceed the fracture strain of aged coatings. Finally, systematic study with pro-active coating condition performance monitoring is discussed.

Nyckelord: ageing; coating fracture; experiments; finite element analysis, water ballast tank

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-10-27. Senast ändrad 2017-06-28.
CPL Pubid: 244270


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för sjöfart och marin teknik, Marin teknik (2015-2017)


Hållbar utveckling
Innovation och entreprenörskap (nyttiggörande)
Sannolikhetsteori och statistik
Annan materialteknik

Chalmers infrastruktur