Direct communication between osteocytes and acid-etched titanium implants with a sub-micron topography

Furqan A. Shah ; Patrik Stenlund ; Anna Martinelli (Institutionen för kemi och kemiteknik, Teknisk ytkemi) ; Peter Thomsen ; Anders Palmquist
Journal of Materials Science-Materials in Medicine (0957-4530). Vol. 27 (2016), 11, p. Article Number: 167.
[Artikel, refereegranskad vetenskaplig]

The osteocyte network, through the numerous dendritic processes of osteocytes, is responsible for sensing mechanical loading and orchestrates adaptive bone remodelling by communicating with both the osteoclasts and the osteoblasts. The osteocyte network in the vicinity of implant surfaces provides insight into the bone healing process around metallic implants. Here, we investigate whether osteocytes are able to make an intimate contact with topologically modified, but micrometre smooth (S-a < 0.5 mu m) implant surfaces, and if sub-micron topography alters the composition of the interfacial tissue. Screw shaped, commercially pure (cp-Ti) titanium implants with (i) machined (Sa = similar to 0.2 mu m), and (ii) two-step acid-etched (HF/HNO3 and H2SO4/HCl; S-a = similar to 0.5 mu m) surfaces were inserted in Sprague Dawley rat tibia and followed for 28 days. Both surfaces showed similar bone area, while the bone-implant contact was 73% higher for the acid-etched surface. By resin cast etching, osteocytes were observed to maintain a direct intimate contact with the acid-etched surface. Although well mineralised, the interfacial tissue showed lower Ca/P and apatite-to-collagen ratios at the acid-etched surface, while mineral crystallinity and the carbonate-to-phosphate ratios were comparable for both implant surfaces. The interfacial tissue composition may therefore vary with changes in implant surface topography, independently of the amount of bone formed. Implant surfaces that influence bone to have higher amounts of organic matrix without affecting the crystallinity or the carbonate content of the mineral phase presumably result in a more resilient interfacial tissue, better able to resist crack development during functional loading than densely mineralised bone.

Nyckelord: bone/implant interface, bone, surface, osseointegration, removal, apatite, orientation, integration, mechanisms, collagen, Engineering, Materials Science



Denna post skapades 2016-10-24. Senast ändrad 2016-11-17.
CPL Pubid: 243886

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kliniska vetenskaper, sektionen för anestesi, biomaterial och ortopedi, Avdelningen för biomaterialvetenskap (GU)
Institutionen för kemi och kemiteknik, Teknisk ytkemi

Ämnesområden

Biomaterialvetenskap

Chalmers infrastruktur