Oxidation Behavior of HVAF-Sprayed NiCoCrAlY Coating in H-2-H2O Environment

E. Sadeghimeresht ; Hamed Hoseini Hooshyar (Institutionen för kemi och kemiteknik, Oorganisk miljökemi) ; N. Markocsan ; S. Joshi ; P. Nylen
Oxidation of Metals (0030-770X). Vol. 86 (2016), 3-4, p. 299-314.
[Artikel, refereegranskad vetenskaplig]

Isothermal oxidation behavior of an HVAF-sprayed NiCoCrAlY coating on AISI 304L was studied in an Ar-10 %H-2-20 %H2O environment at 600 A degrees C. Techniques such as BIB/SEM, EDS, and XRD were used to comprehensively characterize the coating and the coating/substrate interface to investigate the oxidation mechanisms. Results were also compared with those obtained from an uncoated AISI 304L substrate. The alumina-forming NiCoCrAlY coating was found to exhibit superior oxidation behavior due to the formation of a slow-growing and protective Al2O3 scale, while the chromia-forming bare 304L substrate lost its protective capability due to the formation of a duplex [Fe3O4 on (Fe,Cr)(3)O-4 spinel oxide] corrosion product layer.

Nyckelord: HVAF, MCrAlY coating, Oxidation, Water vapor, Oxygen partial pressure



Denna post skapades 2016-10-14.
CPL Pubid: 243417

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Oorganisk miljökemi

Ämnesområden

Kemi

Chalmers infrastruktur