The impact of interfaces in laminated packaging on transport of carboxylic acids

Sofie Gårdebjer (Institutionen för kemi och kemiteknik, Farmaceutisk teknologi ; SuMo Biomaterials) ; Tobias Gebäck (Institutionen för matematiska vetenskaper, matematik ; SuMo Biomaterials) ; Thorbjörn Andersson ; E. Fratini ; P. Baglioni ; Romain Bordes (Institutionen för kemi och kemiteknik, Teknisk ytkemi ; SuMo Biomaterials) ; Anna Viridén ; M. Nicholas ; Niklas Lorén (SuMo Biomaterials ; Institutionen för fysik, Eva Olsson Group (Chalmers)) ; Anette Larsson (Institutionen för kemi och kemiteknik, Farmaceutisk teknologi ; SuMo Biomaterials)
Journal of Membrane Science (0376-7388). Vol. 518 (2016), p. 305-312.
[Artikel, refereegranskad vetenskaplig]

The permeability of oleic and acetic acid through low density polyethylene (LDPE) and ethylene acrylic acid (EAA) have been measured using diffusion cells. In addition, the permeability through combinations of LDPE and EAA in the form of laminates with different numbers of layers has been determined. Oleic acid shows an almost 30 times higher permeability compared to acetic acid, which was partly explained by the adsorption of oleic acid to the film surface during the permeability experiment. In addition, the permeability is lower for both oleic and acetic acid in the laminates compared to the pure films. The decreased permeability can be explained by the presence of crystalline domains close to the interface. This is supported by SAXS data which suggests an ordering of polymer chains in the EAA film close to the interface. In summary, the results show that it is possible to create barrier materials with decreased permeability, which is interesting for example in the packaging industry. (C) 2016 Elsevier B.V. All rights reserved.

Nyckelord: Permeability, Laminates, Interfaces, Polymers, Packaging, barrier properties, molecular-weight, permeability, polyethylene, polypropylene, films, copolymers, vapors, issues, gases, Engineering, Polymer Science



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-09-30. Senast ändrad 2017-01-27.
CPL Pubid: 242728

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Farmaceutisk teknologi
SuMo Biomaterials
Institutionen för matematiska vetenskaper, matematik (2005-2016)
Institutionen för kemi och kemiteknik, Teknisk ytkemi
Institutionen för fysik, Eva Olsson Group (Chalmers)

Ämnesområden

Materialvetenskap
Kemi

Chalmers infrastruktur