Temperature-dependent evolution of the cyclic yield stress of railway wheel steels

Johan Ahlström (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; Elena Kabo (Institutionen för tillämpad mekanik, Material- och beräkningsmekanik) ; Anders Ekberg (Institutionen för tillämpad mekanik, Dynamik)
Wear (0043-1648). Vol. 366 (2016), SI, p. 378-382.
[Artikel, refereegranskad vetenskaplig]

The evolution of the cyclic yield stress for a railway wheel steel (UIC ER7T) during cyclic plastic straining has been characterized at different temperatures from -60 to 600 °C. Different constant strain amplitude levels were examined and for temperatures above 200 °C, hold periods were included to study stress relaxation during constant compressive strain. The results are of use in predicting material deformation and damage. This is demonstrated by the application to improve a criterion for surface initiated rolling contact fatigue damage.

Nyckelord: Rolling contact fatigue; Ratcheting; Low cycle fatigue; Stress–strain loop; Thermal effects

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-06-27. Senast ändrad 2017-03-21.
CPL Pubid: 238319


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Materialteknologi (2005-2017)
Institutionen för tillämpad mekanik, Material- och beräkningsmekanik (2005-2017)
Institutionen för tillämpad mekanik, Dynamik (1900-2017)


Övrig teknisk mekanik
Övrig teknisk materialvetenskap

Chalmers infrastruktur