Space charge limited current mechanism in Bi2S3 nanowires

G. Kunakova ; R. Viter ; Simon Abay (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; S. Biswas ; J. D. Holmes ; Thilo Bauch (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; Floriana Lombardi (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; D. Erts
Journal of Applied Physics (0021-8979). Vol. 119 (2016), 11,
[Artikel, refereegranskad vetenskaplig]

We report on the charge transport properties of individual Bi2S3 nanowires grown within the pores of anodized aluminum oxide templates. The mean pore diameter was 80 nm. Space charge limited current is the dominating conduction mechanism at temperatures below 160 K. Characteristic parameters of nanowires, such as trap concentration and trap characteristic energy, were estimated from current-voltage characteristics at several temperatures.

Nyckelord: electrical characterization, temperature-dependence, gaas nanowires, single, memristor, density, arrays, transport, crystals, growth