Microstructural examination of shear localisation during high-strain-rate deformation of Alloy 718

Joakim Johansson (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; Christer Persson (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; Haiping Lai ; Magnus Hörnqvist Colliander (Institutionen för fysik, Materialens mikrostruktur (Chalmers))
Materials science and engineering A - structural materials properties microstructure and processing (0921-5093). Vol. 662 (2016), p. 363-372.
[Artikel, refereegranskad vetenskaplig]

Chip formation during metal cutting involves high strain rates and large deformations. Under many conditions, the deformation is concentrated in narrow bands due to shear localisation from adiabatic heating. In order to understand the localisation process, it is necessary to increase the knowledge regarding the microstructural evolution during deformation. However, the deformation that occurs during chip formation is hard to measure. Therefore, this study utilises top-hat specimens deformed at high strain rates in order to generate localised shear bands in the Ni-based superalloy Alloy 718, with defined measurable deformation. The resulting shear bands in the top-hat specimens are compared with those generated in metal cutting chips and studied in order to characterise the deformation occurring at a microstructural level. The resulting microstructures in the top-hat specimens and machining chips are found to be similar, with heavily localised deformation into narrow shear bands and homogeneously sheared microstructure adjacent to the bands. The centres of the shear bands are heavily deformed with ultra-fine grains, indicating dynamic recrystallisation during the deformation. The results indicate that the shear deformation produced by high strain rate testing of top-hat specimens can provide an excellent means of replicating the conditions for shear localisation during metal cutting. However, care should be taken to design the tests so that the local conditions are representative in terms of strains and strain rates.

Nyckelord: Nickel-based superalloy; Adiabatic shear bands; Dynamic recrystallisation; Metal cutting; Electron microscopy; Split-Hopkinson pressure bar

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-03-18. Senast ändrad 2017-03-02.
CPL Pubid: 233437


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Materialteknologi (2005-2017)
Institutionen för fysik, Materialens mikrostruktur (Chalmers)



Chalmers infrastruktur