Coarsening of Pd nanoparticles in an oxidizing atmoshere studied by in situ TEM

Søren Bredmose Simonsen ; Ib Chorkendorff ; Søren Dahl ; Magnus Skoglundh (Kompetenscentrum katalys (KCK) ; Institutionen för kemi och kemiteknik, Teknisk ytkemi) ; Stig Helveg
Surface Science (0039-6028). Vol. 648 (2016), p. 278-283.
[Artikel, refereegranskad vetenskaplig]

The coarsening of supported palladiumnanoparticles in an oxidizing atmospherewas studied in situ by means of transmission electron microscopy (TEM). Specifically, the Pd nanoparticles were dispersed on a planar and amorphous Al2O3 support and were observed during the exposure to 10 mbar technical air at 650 °C. Time-resolved TEM image series reveal that the Pd nanoparticles were immobile and that a few percent of the nanoparticles grew or shrank, indicating a coarsening process mediated by the Ostwald ripening mechanism. The TEM image contrast suggests that the largest nanoparticles tended to wet the Al2O3 support to a higher degree than the smaller nanoparticles and that the distribution of projected particle sizes consequently broadens by the appearance of an asymmetric tail toward the larger particle sizes. A comparison with computer simulations based on a simple mean-fieldmodel for the Ostwald ripening process indicates that the observed change in the particle size distribution can be accounted for by wetting of the Al2O3 support by the larger Pd nanoparticles.

Nyckelord: Sintering; Coarsening; Ostwald ripening; Palladium; In situ TEM; Catalyst deactivation

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-03-16. Senast ändrad 2016-05-27.
CPL Pubid: 233278


Läs direkt!

Länk till annan sajt (kan kräva inloggning)