Investigation to the deep center related properties of low temperature grown InPBi with Hall and photoluminescence

P. Wang ; W. Pan ; K. Wang ; X. Wu ; L. Yue ; Q. Gong ; Shumin Wang (Institutionen för mikroteknologi och nanovetenskap, Fotonik)
AIP Advances Vol. 5 (2015), 12, p. Art. no. 127104.
[Artikel, refereegranskad vetenskaplig]

InP1-xBix epilayers with bismuth (Bi) concentration x= 1.0% were grown on InP by gas source molecular beam epitaxy (GS-MBE) at low temperature (LT). Bi incorporation decreased the intrinsic free electron concentration of low temperature grown InP indicated by hall analysis. It is concluded that deep level center was introduced by Bi. Influence of Si doping on the InP1-xBix films Photoluminescence (PL) was investigated. N-type doping in the InP1-xBix epilayers was found to be effective at PL enhancement. Blue shift of InPBi PL emission wavelength was observed as the Si doping concentration increasing. Two independent peaks were fitted and their temperature dependence behavior was observed to be distinct obviously. Two individual radiative recombination processes were expected to be involved.

Denna post skapades 2016-03-09. Senast ändrad 2016-07-05.
CPL Pubid: 232948


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Fotonik



Chalmers infrastruktur