Cold cathode emission studies on topographically modified few layer and single layer MoS2 films

A.P.S. Gaur ; S. Sahoo ; F. Mendoza ; A.M. Rivera ; M. Kumar ; Saroj Prasad Dash (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik) ; G. Morell ; R.S. Katiyar
Applied Physics Letters (0003-6951). Vol. 108 (2016), p. 043103.
[Artikel, refereegranskad vetenskaplig]

Nanostructured materials, such as carbon nanotubes, are excellent cold cathode emitters. Here, we report comparative field emission (FE) studies on topographically tailored few layer MoS2films consisting of ⟨0001⟩ plane perpendicular (⊥) to c-axis (i.e., edge terminated vertically aligned) along with planar few layer and monolayer (1L) MoS2films. FE measurements exhibited lower turn-on field Eto (defined as required applied electric field to emit current density of 10 μA/cm2) ∼4.5 V/μm and higher current density ∼1 mA/cm2, for edge terminated vertically aligned (ETVA) MoS2films. However, Eto magnitude for planar few layer and 1L MoS2films increased further to 5.7 and 11 V/μm, respectively, with one order decrease in emission current density. The observed differences in emission behavior, particularly for ETVA MoS2 is attributed to the high value of geometrical field enhancement factor (β), found to be ∼1064, resulting from the large confinement of localized electric field at edge exposed nanograins. Emission behavior of planar few layers and 1L MoS2films are explained under a two step emission mechanism. Our studies suggest that with further tailoring the microstructure of ultra thin ETVA MoS2films would result in elegant FE properties.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-03-03. Senast ändrad 2016-05-30.
CPL Pubid: 232749


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)