Characterisation of the mechanical and fracture properties of a uni-weave carbon fibre/epoxy non-crimp fabric composite

Thomas Bru (Institutionen för tillämpad mekanik, Material- och beräkningsmekanik) ; Peter Hellström ; Renaud Gutkin ; Dimitra Ramantani ; Göran Peterson
Data In Brief (2352-3409). Vol. 6 (2016), p. 680-695.
[Artikel, refereegranskad vetenskaplig]

A complete database of the mechanical properties of an epoxy polymer reinforced with uni-weave carbon fibre non-crimp fabric (NCF) is established. In-plane and through-the-thickness tests were performed on unidirectional laminates under normal loading and shear loading. The response under cyclic shear loading was also measured. The material has been characterised in terms of stiffness, strength, and failure features for the different loading cases. The critical energy release rates associated with different failure modes in the material were measured from interlaminar and translaminar fracture toughness tests. The stress–strain data of the tensile, compressive, and shear test specimens are included. The load–deflection data for all fracture toughness tests are also included. The database can be used in the development and validation of analytical and numerical models of fibre reinforced plastics (FRPs), in particular FRPs with NCF reinforcements.

Nyckelord: Polymer matrix composite; Carbon fibre; Non-crimp fabric; Mechanical testing; Mechanical properties; Stress/strain curve; Fracture toughness


Open Access



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-02-15. Senast ändrad 2016-03-24.
CPL Pubid: 232012

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)