Parameters influencing the initial setting time of alkali-activated ground granulated blastfurnace slag materials

Helén Jansson (Institutionen för bygg- och miljöteknik, Byggnadsteknologi) ; Luping Tang (Institutionen för bygg- och miljöteknik, Byggnadsteknologi)
Nordic Concrete Research (0800-6377). Vol. 52 (2015), p. 63-76.
[Artikel, refereegranskad vetenskaplig]

Various parameters influencing the initial setting time of alkali-activated slag materials have been investigated using the Vicat method. The alkali solutions used for the activation were liquid sodium silicate (water glass) of different moduli n (SiO2/Na2O ratio) and pH. The results indicate that the initial setting time is mainly influenced by two parameters; 1) the specific surface area of the slag and 2) the modulus of the solution. The results also suggest that the problem with controlling the initial setting time of alkali-activated slag can be solved by controlling the characteristics of the solvent used for the activation.

Nyckelord: alkali-activation, initial setting time, water glass modulus, sodium silicate solution, pH, specific surface area



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-01-18. Senast ändrad 2016-01-20.
CPL Pubid: 230879

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)