Interparticle Neck Connections in Innovative Insulated Iron Powder Compounds

Robert Bidulsky ; Jana Bidulska ; Raquel de Oro Calderon (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Eduard Hryha (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; Marco Maccarini ; Illaria Forno ; Marco Actis Grande
Acta Physica Polonica. A (0587-4246). Vol. 128 (2015), 4, p. 647-650.
[Artikel, refereegranskad vetenskaplig]

Goal of the present paper is the analysis of the interparticle neck connections in a system made of insulated iron powder compounds with different additions of an Al-Mg-Si-Cu alloy (0.25, 0.5 and 0.75 wt%). The introduction of the aluminium alloy powder has been made in order to improve the mechanical properties, evaluated as the transverse rupture strength, without decreasing the agnetic properties (evaluated in terms of iron loss and coercivity force). The fracture analysis of investigated systems puts into evidence the breaking of interparticle neck connections. Heat treatment (at the temperature of 500C) contributes to the early stages of interparticle neck developments. The chosen aluminium alloy presents a sort of pre-sintering behaviour at 500C, with the possibility of mass-transport processes around the insulated iron powder compounds. The air heat treatment applied aims at providing an increase in the mechanical behaviour of the material, with a final good rigidity after the cooling process. Fracture surfaces and transverse rupture strength values show that, at 500 MPa, the strength and the area related to the inter-particle necks can be correlated to the occasional broken insulated point-to-point surfaces that hinder the development of inter-particles necks.

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2016-01-02. Senast ändrad 2016-01-15.
CPL Pubid: 229402


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Hållbar utveckling
Kompositmaterial och -teknik
Metallurgisk process- och produktionsteknik

Chalmers infrastruktur