A High Performance Ag Alloyed Nano-scale n-type Bi2Te3 Based Thermoelectric Material

Si Chen (Institutionen för mikroteknologi och nanovetenskap, Elektronikmaterial och system ) ; Nikolaos Logothetis (Institutionen för mikroteknologi och nanovetenskap, Elektronikmaterial och system ) ; L. Ye ; Johan Liu (Institutionen för mikroteknologi och nanovetenskap, Elektronikmaterial och system )
Materials Today: Proceedings (2214-7853). Vol. 2 (2015), 2, p. 610-619.
[Konferensbidrag, refereegranskat]

A silver alloyed n-type bismuth telluride (Bi2Te3) thermoelectric (TE) bulk material with nano crystalline structure was studied and characterized in this paper. The Bi2Te3 nanopowders used in this study were first fabricated via a patented explosion based process. Then, the various concentrations of Ag nanoparticles (0-20 wt. %) were added into the Bi2Te3 nanopowders in order to increase the electrical conductivity. Combining the benefits of high electrical conductivity (1.51x10(5) S.m(-1)) and low thermal conductivity (0.441 W.m(-1).K-1), the dimensionless figure of merit (ZT value) of 1.48 for this n-type Bi2Te3 TE material is achieved at 300 K temperature.

Nyckelord: Bismuth-Telluride, Nano-scale, Nanoparticles, Silver, Thermoelectric



Denna post skapades 2015-12-04. Senast ändrad 2017-08-18.
CPL Pubid: 227292

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Elektronikmaterial och system

Ämnesområden

Nanoteknik

Chalmers infrastruktur