Graphene GaN-Based Schottky Ultraviolet Detectors

K. Xu ; C. Xu ; Y. Y. Xie ; J. Deng ; Y. X. Zhu ; W. L. Guo ; M. Xun ; K. B. K. Teo ; H. D. Chen ; Jie Sun (Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik)
Ieee Transactions on Electron Devices (0018-9383). Vol. 62 (2015), 9, p. 2802-2808.
[Artikel, refereegranskad vetenskaplig]

Graphene GaN-based Schottky ultraviolet detectors are fabricated. The monolayer graphene is grown by chemical vapor deposition. The graphene is much more transparent than metals, as confirmed by the fact that our devices retain their high responsivity up to 360-nm wavelength (corresponding to the band edge absorption of GaN). Importantly, by virtue of the tunable work function of graphene, the graphene GaN Schottky barrier height can be greatly enlarged. The built-in field is enhanced, and the detector performance is improved. The current ratio with and without luminescence is up to 1.6 x 10(4). The characteristic time constants of the devices are in the order of a few milliseconds. The device open-circuit voltage and short-circuit current are also increased. At last, special type Schottky devices consisting of GaN nanorods or surface-etched GaN are prepared for complementary study. It is found although the dry etching induced surface defects lead to an increase in the dark current, and these carrier traps also greatly contribute to the photoconductivity under luminescence, resulting in extraordinarily large responsivity (up to 360 A/W at -6 V).

Nyckelord: GaN, graphene, Schottky ultraviolet (UV) detectors



Denna post skapades 2015-09-17.
CPL Pubid: 222709

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för mikroteknologi och nanovetenskap, Kvantkomponentfysik

Ämnesområden

Annan materialteknik
Nanoteknik

Chalmers infrastruktur