Deformation at ambient and high temperature of in situ Laves phases-ferrite composites

P. Donnadieu ; C. Pohlmann ; S. Scudino ; J.J. Blandin ; Kumar Babu Surreddi (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; J. Eckert
Science and Technology of Advanced Materials (1468-6996). Vol. 15 (2014), 3,
[Artikel, refereegranskad vetenskaplig]

The mechanical behavior of a Fe80Zr10Cr10 alloy has been studied at ambient and high temperature. This Fe 80Zr10Cr10 alloy, whoose microstructure is formed by alternate lamellae of Laves phase and ferrite, constitutes a very simple example of an in situ CMA phase composite. The role of the Laves phase type was investigated in a previous study while the present work focuses on the influence of the microstructure length scale owing to a series of alloys cast at different cooling rates that display microstructures with Laves phase lamellae width ranging from ∼50 nm to ∼150 nm. Room temperature compression tests have revealed a very high strength (up to 2 GPa) combined with a very high ductility (up to 35%). Both strength and ductility increase with reduction of the lamella width. High temperature compression tests have shown that a high strength (900 MPa) is maintained up to 873 K. Microstructural study of the deformed samples suggests that the confinement of dislocations in the ferrite lamellae is responsible for strengthening at both ambient and high temperature. The microstructure scale in addition to CMA phase structural features stands then as a key parameter for optimization of mechanical properties of CMA in situ composites. © 2014 National Institute for Materials Science.

Nyckelord: complex metallic alloys , in situ composites , mechanical behavior , metal matrix composites



Denna post skapades 2015-05-06.
CPL Pubid: 216643

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)

Ämnesområden

Mekanisk energiteknik

Chalmers infrastruktur