Study on fracture of the fibrous monolith cemented carbide

C. Ding ; X. Liu ; Y. Li ; Changhai Li (Institutionen för material- och tillverkningsteknik, Materialteknologi) ; N. Li ; F. Li
Advanced Materials Research (1022-6680). Vol. 815 (2013), p. 43-47.
[Artikel, refereegranskad vetenskaplig]

A fibrous monolith cemented carbide with WC-6%Co as cell and WC-20%Co as cell boundaries was produced through hot co-extrusion process in this paper. The density, hardness, transverse rupture strength (TRS) and fracture toughness (KIc) of the fibrous monolith cemented carbide were tested, and the fracture and crack propagation were observed by metalloscope and Scanning Electron Microscope. The result shows fibrous monolith structure design could effectively improve the TRS and the KIc of WC/Co cemented carbide without a significant decrease of hardness. It is the reason of high transverse rupture strength and fracture toughness that WC-20%Co can absorb more fracture energy in order to slow, prevent, or deflect crack propagation, proved by metalloscope and scanning electron microscope.

Nyckelord: Cemented carbide, Fibrous monolith, Fracture, Toughness

Denna post skapades 2015-05-05.
CPL Pubid: 216427


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Materialteknologi (2005-2017)



Chalmers infrastruktur