Nanostructure of a cubic BN cutting tool material

Jenny Angseryd ; Fang Liu (Institutionen för teknisk fysik, Materialens mikrostruktur ) ; Hans-Olof Andrén (Institutionen för teknisk fysik, Materialens mikrostruktur )
International journal of refractory metals & hard materials (0958-0611). Vol. 49 (2015), p. 283-287.
[Artikel, refereegranskad vetenskaplig]

Advanced microscopy techniques, laser assisted atom probe tomography and electron energy loss spectroscopy in transmission electron microscopy are used to investigate in detail the microstructure of a polycrystalline cubic boron nitride tool material. During sintering at high pressure superhard cubic boron nitride combines with hard ceramic Ti(C,N) to form a dense material. Diffusion in Ti(C,N) and reactions between Ti(C,N), cBN and additives result in the formation of several nitride, oxide and boride phases in a complex mixed microcrystalline and nano- crystalline microstructure.



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2015-04-08. Senast ändrad 2016-01-20.
CPL Pubid: 214918

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för teknisk fysik, Materialens mikrostruktur (2012-2015)

Ämnesområden

Materialvetenskap
Materialteknik
Kompositmaterial och -teknik
Bearbetnings-, yt- och fogningsteknik
Metallurgi och metalliska material

Chalmers infrastruktur