Comprehensive study of Mn–Fe–Al oxygen-carriers for chemical-looping with oxygen uncoupling (CLOU)

Golnar Azimi (Institutionen för kemi och kemiteknik, Oorganisk miljökemi) ; Tobias Mattisson (Institutionen för energi och miljö, Energiteknik) ; Henrik Leion (Institutionen för kemi och kemiteknik, Oorganisk miljökemi) ; Magnus Rydén (Institutionen för energi och miljö, Energiteknik) ; Anders Lyngfelt (Institutionen för energi och miljö, Energiteknik)
International Journal of Greenhouse Gas Control (1750-5836). Vol. 34 (2015), p. 12-24.
[Artikel, refereegranskad vetenskaplig]

The reactivity and attrition resistance of Mn–Fe oxygen carriers with addition of Al2O3 as support have been investigated. Spray-dried oxygen-carrier particles with Mn:Fe molar ratios of 80:20 and 33:67 were prepared using different amounts of Al2O3. Each material was calcined for 4 h at 950 °C, 1100 °C or 1200 °C. The oxygen carriers were studied in a batch fluidized bed reactor to investigate their reactivity with wood char, CH4, syngas and also their oxygen release in N2. In order to measure the mechanical stability of the different materials, the attrition resistance was measured in a jet-cup apparatus. Addition of Al2O3 to materials with a Mn:Fe molar ratio of 80:20 was not advantageous. Generally oxidation of these materials was problematic. The Al2O3 supported materials with a Mn:Fe molar ratio of 80:20 calcined at 950 °C and 1100 °C showed poor attrition resistance and were highly fragmented or turned to dust, whereas those calcined at 1200 °C showed high attrition resistance but poor gas conversion.Materials with a Mn:Fe molar ratio of 33:67 supported with Al2O3 generally showed better attrition resistance. Also their oxidation with 5 vol% of oxygen was possible at temperatures higher than 850 °C. Furthermore, some of these materials showed good reactivity with methane, syngas and char. Low attrition, good reactivity and CLOU properties in combination with potentially low raw materials costs, make these materials interesting for CLC.

Nyckelord: CO2 capture, Chemical-looping combustion, Chemical-looping with oxygen uncoupling, Iron manganese oxide, Al2O3

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2015-01-27. Senast ändrad 2017-10-03.
CPL Pubid: 211551


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för kemi och kemiteknik, Oorganisk miljökemi
Institutionen för energi och miljö, Energiteknik (2005-2017)


Hållbar utveckling

Chalmers infrastruktur