Mineralogical, Physical and Chemical Characterization of Cementitious Materials Subjected to Accelerated Decalcification by an Electro-Chemical Method

Arezou Babaahmadi (Institutionen för bygg- och miljöteknik) ; Luping Tang (Institutionen för bygg- och miljöteknik, Byggnadsteknologi) ; Zareen Abbas (Institutionen för kemi- och bioteknik)
Nordic Concrete Research (0800-6377). Vol. 1/2014 (2014), 49, p. 181-198.
[Artikel, refereegranskad vetenskaplig]

To facilitate the service life predictions regarding durability of nuclear waste repositories acceleration methods enhancing the decalcification process are needed. In this study an electro-chemical migration method to accelerate leaching of calcium from cementitious specimens of sizes 50×100Ø and 75×50Ø mm is presented. The mineralogical, physical and chemical properties of degraded samples are characterized. The results demonstrate that up to 70% decrease in strength, 50 % decrease in E-modulus, 90 % increase in gas permeability, at least 70% increase in chloride diffusion coefficient and 70 % increase in pore volume could be expected due to leaching of portlandite from concrete.

Nyckelord: Acceleration method, Calcium leaching, Service life, Mineralogical properties, Diffusion, Adsorption, Mechanical Properties, Permeability

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2015-01-26. Senast ändrad 2017-03-21.
CPL Pubid: 211525


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Institutioner (Chalmers)

Institutionen för bygg- och miljöteknik (2005-2017)
Institutionen för bygg- och miljöteknik, Byggnadsteknologi (2005-2017)
Institutionen för kemi- och bioteknik (2005-2014)


Building Futures

Chalmers infrastruktur