Effect of TiO2 nano-filler and EC plasticizer on electrical and thermal properties of poly(ethylene oxide) (PEO) based solid polymer electrolytes

K. Vignarooban ; M. A. K. L. Dissanayake ; Ingvar Albinsson ; Bengt-Erik Mellander (Institutionen för teknisk fysik, Nukleär teknik)
SOLID STATE IONICS (0167-2738). Vol. 266 (2014), p. 25-28.
[Artikel, refereegranskad vetenskaplig]

Ionic conductivity of poly(ethylene oxide)-lithium trifluoromethanesulfonate (LiCF3SO3 or LiTf) based polymer electrolyte has been increased by incorporating TiO2 nano-filler. Incorporation of 10 wt.% TiO2 exhibited the highest conductivity enhancement with a value of 4.9 x 10(-5) S cm(-1) at 30 degrees C. A further enhancement in conductivity to a value of 1.6 x 10(-4)S cm(-1) at 30 degrees C has been obtained by the incorporation of 50 wt.% ethylene carbonate (EC) plasticizer. Both additives cause a reduction of the PEO crystalline phase content and an increased segmental flexibility leading to conductivity enhancement.

Nyckelord: Nano-composite polymer electrolytes; Plasticizers; TiO2 nano-fillers; Ionic conductivity enhancement



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2015-01-09. Senast ändrad 2016-03-08.
CPL Pubid: 210330

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för fysik (GU) (GU)
Institutionen för teknisk fysik, Nukleär teknik (2006-2015)

Ämnesområden

Energi
Materialvetenskap
Nanovetenskap och nanoteknik
Hållbar utveckling
Den kondenserade materiens fysik
Nanoteknik

Chalmers infrastruktur