Tin clustering and precipitation in the oxide during autoclave corrosion of Zircaloy-2

Gustav Sundell (Institutionen för teknisk fysik, Materialens mikrostruktur ) ; Mattias Thuvander (Institutionen för teknisk fysik, Materialens mikrostruktur ) ; Hans-Olof Andrén (Institutionen för teknisk fysik, Materialens mikrostruktur )
Journal of Nuclear Materials (0022-3115). Vol. 456 (2015), p. 409-414.
[Artikel, refereegranskad vetenskaplig]

Atom probe tomography has been used to study the evolution of tin distribution during the corrosion process in Zircaloy-2. From being completely soluble in the Zr metal matrix, some clustering is evident already in the newly formed oxide close to the metal-oxide interface. Analysis of thicker oxides a few hundred nanometers away from the interface reveals fully developed precipitates of metallic Sn particles of up to 20 nm in size. Although the precipitates contain significant amounts of Zr, it is concluded that they are in the process of being depleted in Zr, which is limited only by the slow diffusion in the oxide scale. The findings are interpreted as being a result of the nobility of the Sn yielding a strong driving force to remain in a metallic state after incorporation in the barrier oxide layer. As Sn occupies substitutional sites in the ZrO2 lattice it is oxidized to a 4+ state when incorporated into the oxide, and in order to remain metallic it must nucleate into precipitates within the inner part of the oxide scale before being re-oxidized to 2+ and eventually to 4+ when the oxygen activity is sufficiently high in the outer parts of the oxide.

Nyckelord: Zircaloy-2, corrosion, precipitation, atom probe tomography, Sn, zirconium oxide

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2014-12-02. Senast ändrad 2015-03-30.
CPL Pubid: 207113


Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för teknisk fysik, Materialens mikrostruktur (2012-2015)



Chalmers infrastruktur

Relaterade publikationer

Denna publikation ingår i:

Atomic Scale Degradation of Zirconium Alloys for Nuclear Applications