Precipitate evolution in the early stages of ageing in Inconel 718 investigated using small-angle x-ray scattering

M. Fisk ; Joel Andersson (Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik) ; R. du Rietz ; S. Haas ; S. Hall
Materials Science & Engineering: A (0921-5093). Vol. 612 (2014), p. 202-207.
[Artikel, refereegranskad vetenskaplig]

Microstructural evolution during the early stages of ageing (less than one hour) in a Ni-Cr-Fe based superalloy Inconel 718 (IN718) has been investigated using Small-Angle X-ray Scattering (SAXS). The effects of precipitate kinetics on the precipitate size distribution are compared indirectly with SAXS measurements by using Vickers microhardness data. The microhardness increased after 4 min of ageing at a temperature of 760 degrees C, although the recorded SAXS data did not reveal the precipitate size distribution. This indicates that the precipitates had not evolved enough to be detected, but still a small number of precipitates increased the yield strength. After ageing the alloy for the shortest period for which data were available, 8 min, clear evidence of precipitates could be found from the SAXS data, showing that the gamma '' - precipitates are about 6 nm in width and 3 nm in height.

Nyckelord: Nucleation, SAXS, Vickers microhardness, Nickel based superalloys, Age hardening, IN718

Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2014-09-15. Senast ändrad 2015-09-17.
CPL Pubid: 202745


Läs direkt!

Länk till annan sajt (kan kräva inloggning)

Institutioner (Chalmers)

Institutionen för material- och tillverkningsteknik, Yt- och mikrostrukturteknik (2005-2017)


Metallurgi och metalliska material

Chalmers infrastruktur