Surface structure and mechanical properties of impaction-modified Y-TZP

E. Papia ; R. Jimbo ; B. R. Chrcanovic ; Martin Andersson (Institutionen för kemi- och bioteknik, Teknisk ytkemi) ; P. V. von Steyern
Dental Materials (0109-5641). Vol. 30 (2014), 8, p. 808-816.
[Artikel, refereegranskad vetenskaplig]

Objectives. The objectives of the study were to describe the surface structure and the chemical surface composition of Y-TZP ceramics produced by using the modified additive technique and to evaluate the flexural strength of Y-TZP with or without surface modification and with different pretreatments: etching before or after sintering combined with or without an adhesive cement system. Methods. Y-TZP discs were used for surface analysis (n=48) and for biaxial flexural strength testing (n= 200). The specimens were divided into groups depending on the cementation surface of Y-TZP: unmodified, sandblasted or glass-modified Y-TZP surfaces, and according to the production process: etching before or after sintering. Results. The surface structure and the chemical composition of glass-modified Y-TZP differ; a rougher surface and phase transformation was identified compared to unmodified Y-TZP. The unmodified Y-TZP groups showed significantly higher flexural strength compared to the glass-modified groups (p <0.001) and showed increased flexural strength after sandblasting (p <0.001). Furthermore, by adding cement to the surface, the value increased even further in comparison with the sandblasted non-cemented specimens (p <0.01). After thermocycling, however, the cement layer on the unmodified and the sandblasted surfaces had air pockets and regions with loose cement. Signcance. A rougher surface structure, superficial glass remnants and a higher content of m-phase was present in the cementation surface of glass-modified Y-TZP. The glass modification creates a bondable cementation surface that is durable. By etching the glass-modified Y-TZP before sintering, a more homogenous surface is created compared to one that is etched after sintering.

Nyckelord: Compressive strength, Dental bonding, Dental cements, Dental ceramics, Materials testing, Yttria-, flexural strength, clinical-performance, ceramic restorations, stabilized zirconia, fracture-toughness, dental prostheses, bond, strength, resin cement, oxide, selection



Denna post skapades 2014-09-12. Senast ändrad 2014-09-12.
CPL Pubid: 202680

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Teknisk ytkemi (2005-2014)

Ämnesområden

Materialteknik
Odontologi

Chalmers infrastruktur