Comparison of carrier scattering mechanisms in chemical vapor deposited graphene on fused silica and strontium titanite substrates

Michael Andersson (Institutionen för mikroteknologi och nanovetenskap, Terahertz- och millimetervågsteknik ) ; Andrei Vorobiev (Institutionen för mikroteknologi och nanovetenskap, Terahertz- och millimetervågsteknik ) ; Spartak Gevorgian (Institutionen för mikroteknologi och nanovetenskap, Terahertz- och millimetervågsteknik ) ; Jan Stake (Institutionen för mikroteknologi och nanovetenskap, Terahertz- och millimetervågsteknik )
Graphene Week 2014 (2014)
[Konferensbidrag, refereegranskat]

Graphene is explored for numerous applications for both electronics and photonics. These range from high frequency and low noise field effect transistors to conductive and highly transparent LED electrodes. To exploit the full potential of graphene, the remarkable intrinsic carrier transport properties and tunable, potentially low sheet resistance must be efficiently utilized. However, graphene carrier mobility is currently strongly degraded by extrinsic factors arising mainly from the dielectric environment, i.e. substrate and gate oxide. A proposed route to enhance transport is the use of a high-κ substrate to screen charged impurities at the graphene-substrate interface. In this paper, mobility and carrier concentration in CVD grown graphene films on fused silica (FS, κ=3.9) and strontium titanite (STO, κ=300) substrates are extracted from microwave measurements and compared to Hall data. To model the mobilities scattering by charged impurities (CI), substrate polar phonons (SPP) and resonant centers (RS) are included. Resonant scatterers dominates on strontium titanite and together with charged impurities on fused silica. While resonant scatterers are likely reduced by moving from wet to dry graphene transfer methods, the nominal mobility improvement by screening of charged impurities on high- κ strontium titanite would be masked at room temperature by increased surface phonon scattering.

Nyckelord: Graphene, carrier scattering, mobility, substrate