Synthesis and functionalization of SSZ-13 as NH3-SCR catalyst

Alexander Shishkin (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; Kompetenscentrum katalys (KCK)) ; Hannes Kannisto (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; Kompetenscentrum katalys (KCK)) ; Hanna Härelind Ingelsten (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; Kompetenscentrum katalys (KCK)) ; Per-Anders Carlsson (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; Kompetenscentrum katalys (KCK)) ; Magnus Skoglundh (Institutionen för kemi- och bioteknik, Teknisk ytkemi ; Kompetenscentrum katalys (KCK))
Catalysis Science & Technology (2044-4753). Vol. 4 (2014), p. 3917-3926.
[Artikel, refereegranskad vetenskaplig]

Hydrothermal synthesis of Na-SSZ-13 using a low concentration of the structure-directing agent N,N,N-trimethyl-1-adamantanimonium hydroxide and functionalization of the SSZ-13 framework through the introduction of Cu and Fe via ion-exchange have been carried out. The prepared samples were characterized with XRD, SEM, UV-Vis, N2-sorption, XRF and NH3-TPD. It was found that relatively large iron oxide particles and well-dispersed cationic Cu2+ species are formed as a result of ion-exchange with iron and copper, respectively. Further, the catalytic activity for NH3 oxidation, NO oxidation and selective catalytic reduction of NOx with ammonia (NH3-SCR) was investigated both in absence and presence of water. The functionalization of the SSZ-13 structure enhances the catalytic activity for NH3-SCR significantly. Whilst the NH3-SCR activity is negligible for the Na-SSZ-13 sample, the Cu-SSZ-13 sample is highly active, especially at low temperatures, and for the Fe-SSZ-13 sample highest activity is shown at elevated temperatures.

Nyckelord: Environmental catalysis, exhaust aftertreatment, selective catalytic reduction, SCR, catalyst preparation, ion-exchange, chabazite, zeolite, copper, iron.



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2014-06-30. Senast ändrad 2017-09-14.
CPL Pubid: 199948

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)

Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för kemi- och bioteknik, Teknisk ytkemi (2005-2014)
Kompetenscentrum katalys (KCK)

Ämnesområden

Energi
Materialvetenskap
Nanovetenskap och nanoteknik
Transport
Hållbar utveckling
Spektroskopi
Kemiteknik
Katalys

Chalmers infrastruktur